Fused Magnesia Brick
2.High strength,excellent corrosions resistance,high temperature resistance and good slag and spalling resistance.
3.Mainly used in steel making converter,EAF,glass kiln and nonferrous furnace.
Technical data sheet
|
Item |
DMZ-92 |
DMZ-93 |
DMZ-95 |
DMZ-97 |
DMZ98 |
|
MgO (%) |
≥92 |
≥93 |
≥95 |
≥97 |
≥98 |
|
≤3.0 |
≤2.0 |
≤0.7 |
≤0.5 |
||
|
≤1.0 |
≤0.8 |
≤0.7 |
≤0.6 |
||
|
CaO (%) |
≤2.5 |
≤2.0 |
≤1.5 |
≤1.2 |
≤0.8 |
|
Al2O3 (%) |
≤1.0 |
≤0.8 |
≤0.5 |
≤0.3 |
≤0.3 |
|
Bulk density (g/cm3) |
≥2.95 |
≥2.98 |
≥3.05 |
≥3.1 |
|
|
Apparent porosity (%) |
≤18 |
≤18 |
≤17 |
≤16 |
≤16 |
|
Cold crushing strength (Mpa) |
≥60 |
≥70 |
≥80 |
≥90 |
≥90 |
|
Refractoriness under load, 0.2MPa (°C) |
≥1560 |
≥1580 |
≥1650 |
≥1700 |
≥1700 |
|
(950°C air cooling)Thermal shock resistance |
≥10 |
≥10 |
≥10 |
≥10 |
Features
1.High refractoriness,usually the refractoriness is above 2000°C.
2.Strong ability to resist basic (alkaline) slag,can not contact with acid refractory material.
3.Poor Thermal shock resistance,so keep the temperature of furnace stabilized.
5.Strong ability of thermal conductivity,sometime need insulating material.
6.Hydrability, keep product away from moisture during storage.
Applications
|
1.Iron Steel Industry |
steelmaking furnace lining, ferroalloy furnace, metal mixer furnace lining, converter lining, arc furnace (EAF) wall and furnace bottom, soaking furnace, heating furnace bottom |
|
2.Non-ferrous metallurgical industry |
copper,nickel,lead,zinc,tin smelting furnace lining, refined copper reverberatory furnace,ore electric furnace lining |
|
3.Glass Kiln Industry |
glass furnace regenerator checker |
|
4.Building Material Industry |
lime kiln,cement kiln |
|
5.Refractory Material Industry |
High temperature calcination kiln,shaft kiln and tunnel kiln |