Magnesia Brick
2.High pressure shaping and firing in high temperature 1600-1700°C,
3.High strength value under high temperature,good anti-corrosiveness,wear resistance and good crack resistance.
Technical data sheet
MZ-91 |
MZ-95 |
MZ-96 |
MZ-97 |
MZ98 |
|
MgO (%) |
≥91 |
≥94.5 |
≥95.5 |
≥96.5 |
≥97.5 |
CaO (%) |
≤2.0 |
≤2.0 |
≤2.0 |
≤2.0 |
|
Apparent porosity (%) |
≤20 |
≤18 |
≤17 |
≤17 |
≤17 |
Cold crushing strength (Mpa) |
≥58.8 |
≥45 |
≥45 |
≥50 |
≥50 |
Refractoriness under load, 0.2MPa (°C) |
≥1550 |
≥1650 |
≥1700 |
≥1700 |
≥1700 |
Reheating Linear Change(1650°C,2h) (%) |
0~-0.2 |
0~-0.3 |
0~-0.4 |
0~-0.4 |
0~-0.4 |
Features
1.High refractoriness,usually the refractoriness is above 2000°C.
2.Strong ability to resist basic (alkaline) slag,can not contact with acid refractory material.
3.Poor Thermal shock resistance,so keep the temperature of furnace stabilized.
4.Poor Volume stability at high temperature,must set aside appropriate expansion joint when laying brick.
5.Strong ability of thermal conductivity,sometime need insulating material.
6.Hydrability, keep product away from moisture during storage.
Applications
1.Iron Steel Industry |
steelmaking furnace lining, ferroalloy furnace, metal mixer furnace lining, converter lining, arc furnace (EAF) wall and furnace bottom, soaking furnace, heating furnace bottom |
2.Non-ferrous metallurgical industry |
copper,nickel,lead,zinc,tin smelting furnace lining, refined copper reverberatory furnace,ore electric furnace lining |
3.Glass Kiln Industry |
glass furnace regenerator checker |
4.Building Material Industry |
lime kiln,cement kiln |
5.Refractory Material Industry |
High temperature calcination kiln,shaft kiln and tunnel kiln |