1100℃ Calcium Silicate Insulation Board
1.1100℃ Calcium silicate insulation board is formed by press,using silica fume(microsilica),quartz and lime as raw material,synthesized through dynamic hydrothermal process,reinforced with glass fibre and paper fibre.
2.Amorphous silica fill up interspace between xonotlite crystal,it heighten fire-resistance temperature,mainly for back-up insulation of industrial kiln furnace.
2.Amorphous silica fill up interspace between xonotlite crystal,it heighten fire-resistance temperature,mainly for back-up insulation of industrial kiln furnace.
Technical data sheet
Chemical analysis
|
SiO2 |
47%-48% |
Al2O3 |
0.3%-0.4% |
Fe2O3 |
0.3%-0.4% |
|
CaO |
44%-45% |
MgO |
0.5%-0.7% |
Na2O-K2O |
0.9%-0.12% |
|
Lgnition loss (mainly H2O): 6%-7% |
|||||
|
RS-230 |
RS-250 |
RS-270 |
||||
|
Bulk density |
kg/m3 |
250±10% |
270±10% |
300±10% |
||
|
Flexural strength |
MPa |
≥0.45 |
≥0.50 |
≥0.55 |
≥0.60 |
|
|
Compressive strength |
≥0.80 |
≥0.90 |
≥1.0 |
≥1.1 |
||
|
Thermal conductivity |
W/m.k |
0.085 |
0.095 |
0.098 |
0.102 |
|
|
400℃ |
0.100 |
0.108 |
0.110 |
0.116 |
||
|
600℃ |
0.152 |
0.156 |
0.158 |
0.164 |
||
|
800℃ |
0.214 |
0.216 |
0.218 |
0.226 |
||
|
Service temp. Limit |
℃ |
1100 |
1100 |
1100 |
1100 |
|
|
Linear shrinkage 1050℃×12h |
% |
≤2 |
≤2 |
≤2 |
≤2 |
|
Size
|
Length (mm) |
Width(mm) |
Thickness(mm) |
|
400 |
250 |
|
|
500 |
500 |
25-120 |
|
600 |
300 |
25-120 |
|
1000 |
500 |
25-120 |
|
1000 |
600 |
25-120 |
|
1080 |
950 |
|
|
1220 |
900 |
50-110 |
|
1220 |
1220 |
50-110 |
|
This board can be sawing,drilling,milling,digging.Other sizes also can be customized. |
||