Oxide bonded SiC Plate
2.Its life time is more than 200 cycles,has good thermal-conducting efficiency because of its great thermal-conductivity coefficient,30% energy can be saved when using SiC kiln furniture.
Technical data sheet
|
Item |
Normal |
|
SiC (%) |
≥88 |
|
SiO2 (%) |
|
|
Al2O3 (%) |
<2 |
|
Bulk Density (g/cm3) |
2.75-2.85 |
|
Apparent porosity (%) |
<14 |
|
Compressive strength (MPA) |
>90 |
|
Modulus of rupture at 20℃ (MPA) |
>45 |
|
Modulus of rupture at 1300℃ (MPA) |
>56 |
|
Thermal expansion at 20℃-1000℃ (K-1*10-6) |
4.8 |
|
0.3Mpa Refractoriness under load(℃) |
>1700 |
|
Thermal conductivity at 1200°C (w.m/k) |
14.0 |
|
Working temperature (℃) |
1450 |
|
Item |
L×W×T |
Item |
L×W×T |
Item |
L×W×T |
||
|
1 |
250×410×9 |
13 |
400×650×12 |
25 |
37 |
620×680×15 |
|
|
2 |
14 |
420×450×10 |
26 |
550×700×15 |
38 |
630×720×17 |
|
|
3 |
300×350×10 |
15 |
450×450×12 |
27 |
560×800×15 |
39 |
650×720×17 |
|
4 |
350×480×11 |
16 |
28 |
600×600×15 |
40 |
800×800×20 |
|
|
5 |
17 |
460×500×12 |
29 |
600×660×15 |
41 |
800×1000×20 |
|
|
6 |
370×550×12 |
18 |
480×480×12 |
30 |
600×700×14 |
42 |
Φ310×10 |
|
7 |
400×400×10 |
19 |
480×500×12 |
31 |
600×720×17 |
43 |
Φ320×12 |
|
8 |
400×420×10 |
20 |
500×500×12 |
32 |
600×770×15 |
44 |
Φ345×15 |
|
9 |
400×450×10 |
21 |
500×520×12 |
33 |
600×800×15 |
45 |
Φ396×16 |
|
10 |
400×500×11 |
22 |
500×550×12 |
34 |
610×610×15 |
46 |
Φ440×16 |
|
11 |
400×550×12 |
23 |
500×600×13 |
35 |
610×700×14 |
47 |
Φ460×16 |
|
12 |
400×600×12 |
24 |
500×700×14 |
36 |
620×620×20 |
48 |
Φ500×16 |
|
The thickness can be adjusted and other sizes can be customized according to requirements. |
|||||||
Application
The oxidebondedsilicon carbide(OBSIC) plates are mainly suitable for sintering of sanitary ceramic,
construction ceramic,household ceramic and electric ceramic in tunnel kiln,shuttle kiln and roller
kiln below 1450℃.