1.Carbon fiber reinforced calcium silicate insulation board is developed for the non-ferrous industry used for feeding,casting and molding of molten aluminum and other non-ferrous metals,also can be used for clamping fixture of glass industry. 
2.Its characteristic of non-stick aluminum exerts a large.Superior strength and good processability makes it the preferred material for precision CNC machined parts and complex components.

1.Glass fiber reinforced calcium silicate insulation board is developed for the non-ferrous industry used for feeding,casting and molding of molten aluminum and other non-ferrous metals,also can be used for clamping fixture of glass industry. 
2.Its characteristic of non-stick aluminum exerts a large.Superior strength and good processability makes it the preferred material for precision CNC machined parts and complex components.

1.The density 280-450kgs/m3 of calcium silicate fire-proof board has been developed to provide outstanding service in demanding fire-proof application such as industrial chimney,fireplace,steel structural, tanks, equipment, fire-rated walls and steel or wood fire-proof doors.Double polished surface finishing give a precise specification.

1.1100℃ Calcium silicate insulation board is formed by press,using silica fume(microsilica),quartz and lime as raw material,synthesized through dynamic hydrothermal process,reinforced with glass fibre and paper fibre.
2.Amorphous silica fill up interspace between xonotlite crystal,it heighten fire-resistance temperature,mainly for back-up insulation of industrial kiln furnace.

1.The main constituents of 1000℃ calcium silicate insulation board is xonotlite (quartz and lime as raw materia) and reinforced glass fiber,no asbestos.
2.It is a kind of high efficient energy-saving material with temperature limited 1050℃. 
3.Characterised by low bulk density,high specific strength,superior heat resistance,outstanding thermal insulation,excellent durability,chemical corrosion resistance,easy to be cut by saw and easy installation.

1.The main constituents of 650℃ millipore calcium silicate board is tobermorite and reinforced paper fibre,no asbestos.
2.It is a kind of high efficient energy-saving material with temperature limited 650℃.
3.It has the characteristics of small thermal conductivity, high strength,high temperature,non-flammable, easy to process,no corrosion,no pollution and so on.